Guangzhou Willstrong New Material Holding Co., Ltd
The leading ACP company in China
Add to Cart
Facade Cladding 1100 Pure Aluminum 4MM 0.5MM Silver Color Mirror Aluminum Composite panel
High gloss mirror finish is made by anodic oxidation of the aluminum. It makes the aluminium surface as bright as mirror.
Mirror aluminum composite panel structure is essentially composed of three layers which together along with a covering of highly pressurized mirror like paint (PE or PVDF) combine to form a flat panel that represent art as well as the traditional romanticized look. The two layers of aluminum sheets are bonded together permanently with an internal core of polyethylene which when covered through the paint makes the surface even more flat and highly resistant. Mirror ACM has a class 1 fire rating and shatter resistant properties. ACP can be fabricated and have v-groove introduced for folding. Mirror aluminum composite is available in both a silver and gold finish
Advantage of aluminum composite panel:
A. Light weight, good rigidity, high intensity, strong adhesion
B. Without any toxic materials, firepoof, anti-corrosion
C. Beautiful and delicate colors, good decorative effect
D. Easy to be fabricated to different sizes and shapes
E. Easy and fast installation, easy to recycle, no pollution.
| Panel Thickness | 2~4mm |
| Standard size | 1220*2440mm |
| Aluminum Alloy | AA1100, AA3003, AA5005 |
| Core Layer | PE, Aluminum honeycomb, fr, corrugated aluminum etc.. |
| Width | 1220mm, 1250mm, 1500mm, 1575mm |
| Length | 2440mm, 3200mm, 4000mm, 5600mm |
| Weight | subject to panel thickness |
| Surface on front side | Polyvinylidene Fluoride (PVDF), FEVE, PET |
| Color ranges | refer to WILLSTRONG color chart, or RAL/PANTONE/DULUX color series |
| Glossiness | upon requirements |
| Back side finishes | protective coating |
Packing:
Strong wooden packing or bulk packing
REMARKS: OEM SERVICE IS AVAILABLE
| Physical Data(Extraction from SGS Lab Report) | ||
| No. | Test Item | Result |
| 1 | Pencil Hardness | 2H |
| 2 | Impact Resistance | Impact failure end point:77.5kg.cm |
| 3 | Falling Sand Abrasion | Litres of abrasive: 79.0L |
| Coating Thickness:1.1mil | ||
| Abrasion Resistance: 71.8L/mil | ||
| 4 | Specific Gravity | 1.344 |
| 5 | Shear Strength | 21.8MPa |
| 6 | Heat Deflection Temperature | 114.8 ºC |
| 7 | Peel Strength | 0.98kg/mm |
| 8 | Flexural Modulus | 14060MPa |
| 9 | Tensile Strength | 35.1MPa |
| 10 | Elongation at break | 13% |